Lifetime Assessment for Glass Fiber Reinforced Plastic Gliders

Authors

  • Volker Trappe Federal Institute for Materials Research and Testing
  • Stephan Günzel Federal Institute for Materials Research and Testing
  • Fabian Grasse Federal Institute for Materials Research and Testing
  • Ocke Meister Institute of Aircraft Design and Lightweight Structures, Technical University of Braunschweig

Keywords:

Structures, Materials, Design

Abstract

In a research project fatigue, tests on two identical wing sections that are used as representative substitute components were performed to estimate lifetime enhancement of light-weight aircraft such as general aviation gliders.  Single-step fatigue tests at limit load on one component were compared with spectrum loading on the other.  A characteristic damage behavior was observed.  Local buckling due to high shear loading of the sandwich core of the wing shell caused the main damage.  Even though an intentionally high load level was chosen, no increase of micro-cracking could be detected.  Additionally, no delamination effects in laminates or bondings were observed except the skin-core delamination which caused the buckling effect in the wing shell due to fatigue loading.  Finally, the concept of using representative substructures and accompanying specimen tests is an effective approach for in-service loading investigations and could also be applied to research on wind turbine blades.

Downloads

Published

2010-07-12

Issue

Vol. 34 No. 3 (2010)

Section

Articles

License

CLEARANCE AND LICENSE TO PUBLISH:

This paper is UNCLASSIFIED (for public reasons) and has been cleared by the appropriate agencies, company and government. This paper represents original work by the author(s). No portion of the material is covered by a prior copyright; or for any portion copyrighted, the author has obtained permission for its use.
I hereby license OSTIV to publish this paper and to use it for all of OSTIV's current and future publications uses.